Effect of chromium nitride coating on the corrosion and wear resistance of stainless steel

No Thumbnail Available
Identifiers
URI: https://hdl.handle.net/11556/4609
ISSN: 0169-4332
DOI: 10.1016/S0169-4332(99)00350-5
Publication date
2000-02-02
Authors
Advisors
Journal Title
Journal ISSN
Volume Title
Publisher
Citations
Google Scholar
Export
Research Projects
Organizational Units
Journal Issue
Abstract
Ion beam-assisted deposition (IBAD) technique has been used to deposit chromium nitride on the stainless steel substrates. Characterization and performance of this coating was carried out by a round-robin test at various laboratories. About 300 samples, prepared at Spire, USA, were distributed to 10 different laboratories. Characterization of coated materials, carried out using Rutherford backscattering (RBS), X-ray diffraction (XRD), glancing X-ray diffraction, Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS), confirmed a well-adherent layer of chromium nitride with composition and thickness of Cr0.8N0.2 and 1.2 μm, respectively. The performance of the coating was tested by tribological tests: dynamic micro-indentation, micro-hardness, wear and friction, and corrosion tests. The coating was found to be hard with good wear resistance and had enhanced resistance to corrosion in acid media.
Description
Keywords
General Chemistry , Condensed Matter Physics , General Physics and Astronomy , Surfaces and Interfaces , Surfaces, Coatings and Films
Type
journal article
Citation
Jagielski , J , Khanna , A S , Kucinski , J , Mishra , D S , Racolta , P , Sioshansi , P , Tobin , E , Thereska , J , Uglov , V , Vilaithong , T , Viviente , J , Yang , S Z & Zalar , A 2000 , ' Effect of chromium nitride coating on the corrosion and wear resistance of stainless steel ' , Applied Surface Science , vol. 156 , no. 1 , pp. 47-64 . https://doi.org/10.1016/S0169-4332(99)00350-5