RT Journal Article
T1 Effect of chromium nitride coating on the corrosion and wear resistance of stainless steel
A1 Jagielski, Jacek
A1 Khanna, A. S.
A1 Kucinski, Jacek
A1 Mishra, D. S.
A1 Racolta, P.
A1 Sioshansi, Piran
A1 Tobin, Eric
A1 Thereska, J.
A1 Uglov, Vladimir
A1 Vilaithong, T.
A1 Viviente, J.
A1 Yang, Si Ze
A1 Zalar, Anton
AB Ion beam-assisted deposition (IBAD) technique has been used to deposit chromium nitride on the stainless steel substrates. Characterization and performance of this coating was carried out by a round-robin test at various laboratories. About 300 samples, prepared at Spire, USA, were distributed to 10 different laboratories. Characterization of coated materials, carried out using Rutherford backscattering (RBS), X-ray diffraction (XRD), glancing X-ray diffraction, Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS), confirmed a well-adherent layer of chromium nitride with composition and thickness of Cr0.8N0.2 and 1.2 μm, respectively. The performance of the coating was tested by tribological tests: dynamic micro-indentation, micro-hardness, wear and friction, and corrosion tests. The coating was found to be hard with good wear resistance and had enhanced resistance to corrosion in acid media.
SN 0169-4332
YR 2000
FD 2000-02-02
LK https://hdl.handle.net/11556/4609
UL https://hdl.handle.net/11556/4609
LA eng
NO Jagielski , J , Khanna , A S , Kucinski , J , Mishra , D S , Racolta , P , Sioshansi , P , Tobin , E , Thereska , J , Uglov , V , Vilaithong , T , Viviente , J , Yang , S Z & Zalar , A 2000 , ' Effect of chromium nitride coating on the corrosion and wear resistance of stainless steel ' , Applied Surface Science , vol. 156 , no. 1 , pp. 47-64 . https://doi.org/10.1016/S0169-4332(99)00350-5
DS TECNALIA Publications
RD 31 jul 2024