Browsing by Keyword "Molecular Medicine"
Now showing 1 - 3 of 3
Results Per Page
Sort Options
Item Fluidized Bed Membrane Reactors for Ultra Pure H2 Production - A Step forward towards Commercialization(2016-03-19) Helmi, Arash; Fernandez, Ekain; Melendez, Jon; Pacheco Tanaka, David A.; Gallucci, Fausto; van Sint Annaland, Martin; TECNOLOGÍAS DE HIDRÓGENO; Tecnalia Research & Innovation; TECNOLOGÍA DE MEMBRANAS E INTENSIFICACIÓN DE PROCESOSIn this research the performance of a fluidized bed membrane reactor for high temperature water gas shift and its long term stability was investigated to provide a proof-of-concept of the new system at lab scale. A demonstration unit with a capacity of 1 Nm3/h of ultra-pure H2 was designed, built and operated over 900 h of continuous work. Firstly, the performance of the membranes were investigated at different inlet gas compositions and at different temperatures and H2 partial pressure differences. The membranes showed very high H2 fluxes (3.89E 6 mol m 2 Pa 1 s 1 at 400 C and 1 atm pressure difference) with a H2/N2 ideal perm-selectivity (up to 21,000 when integrating five membranes in the module) beyond the DOE 2015 targets. Monitoring the performance of the membranes and the reactor confirmed a very stable performance of the unit for continuous high temperature water gas shift under bubbling fluidization conditions. Several experiments were carried out at different temperatures, pressures and various inlet compositions to determine the optimum operating window for the reactor. The obtained results showed high hydrogen recovery factors, and very low CO concentrations at the permeate side (in average <10 ppm), so that the produced hydrogen can be directly fed to a low temperature PEM fuel cell.Item Morphology and N2 Permeance of Sputtered Pd-Ag Ultra-Thin Film Membranes(2016-02-10) Fernandez, Ekain; Sanchez-Garcia, Jose Angel; Viviente, J.L.; van Sint Annaland, Martin; Gallucci, Fausto; Pacheco Tanaka, David A.; Tecnalia Research & Innovation; TECNOLOGÍAS DE HIDRÓGENO; TECNOLOGÍA DE MEMBRANAS E INTENSIFICACIÓN DE PROCESOSThe influence of the temperature during the growth of Pd-Ag films by PVD magnetron sputtering onto polished silicon wafers was studied in order to avoid the effect of the support roughness on the layer growth. The surfaces of the Pd-Ag membrane films were analyzed by atomic force microscopy (AFM), and the results indicate an increase of the grain size from 120 to 250–270 nm and film surface roughness from 4–5 to 10–12 nm when increasing the temperature from around 360–510 K. After selecting the conditions for obtaining the smallest grain size onto silicon wafer, thin Pd-Ag (0.5–2-µm thick) films were deposited onto different types of porous supports to study the influence of the porous support, layer thickness and target power on the selective layer microstructure and membrane properties. The Pd-Ag layers deposited onto ZrO2 3-nm top layer supports (smallest pore size among all tested) present high N2 permeance in the order of 10−6 mol•m−2•s−1•Pa−1 at room temperature.Item Recent Advances in Pd-Based Membranes for Membrane Reactors(2017-01-01) Arratibel Plazaola, Alba; Pacheco Tanaka, David A.; Van Sint Annaland, Martin; Gallucci, Fausto; Tecnalia Research & Innovation; TECNOLOGÍA DE MEMBRANAS E INTENSIFICACIÓN DE PROCESOSPalladium-based membranes for hydrogen separation have been studied by several research groups during the last 40 years. Much effort has been dedicated to improving the hydrogen flux of these membranes employing different alloys, supports, deposition/production techniques, etc. High flux and cheap membranes, yet stable at different operating conditions are required for their exploitation at industrial scale. The integration of membranes in multifunctional reactors (membrane reactors) poses additional demands on the membranes as interactions at different levels between the catalyst and the membrane surface can occur. Particularly, when employing the membranes in fluidized bed reactors, the selective layer should be resistant to or protected against erosion. In this review we will also describe a novel kind of membranes, the pore-filled type membranes prepared by Pacheco Tanaka and coworkers that represent a possible solution to integrate thin selective membranes into membrane reactors while protecting the selective layer. This work is focused on recent advances on metallic supports, materials used as an intermetallic diffusion layer when metallic supports are used and the most recent advances on Pd-based composite membranes. Particular attention is paid to improvements on sulfur resistance of Pd based membranes, resistance to hydrogen embrittlement and stability at high temperature.