Schirp, ArneBarrio, Aitor2018-10-05Schirp , A & Barrio , A 2018 , ' Fire retardancy of polypropylene composites reinforced with rice husks: From oxygen index measurements and cone calorimetry to large-scale single-burning-item tests : From oxygen index measurements and cone calorimetry to large-scale single-burning-item tests ' , Journal of Applied Polymer Science , vol. 135 , no. 37 , 46654 , pp. 46654 . https://doi.org/10.1002/app.466540021-8995researchoutputwizard: 11556/583Publisher Copyright: © 2018 Wiley Periodicals, Inc.Rice husks containing 12 wt % inorganic silica were incorporated together with halogen‐free fire retardants in a polypropylene matrix and extruded into facade profiles. An increase in the amount of rice husks resulted in an increase in the oxygen index. The cone calorimetry measurements showed that all of the fire retardants tested significantly reduced the peak heat‐release rate (pHRR) and maximum average rate of heat emission (MARHE) of the formulations and moderately reduced total heat release. The best results in terms of MARHE were achieved for the formulation including 24% melamine‐coated ammonium polyphosphate. pHRR and MARHE were reduced with increasing amount of rice husks. Single‐burning‐item (SBI) tests were performed for the extruded profiles based on rice husks and, for comparison, wood flour. In the best case, a B‐s2, d0 classification was obtained. The results obtained from cone calorimetry and SBI tests were in agreement. Inc. J. Appl. Polym. Sci. 2018, 135, 46654.11586226enginfo:eu-repo/semantics/restrictedAccessFire retardancy of polypropylene composites reinforced with rice husks: From oxygen index measurements and cone calorimetry to large-scale single-burning-item tests: From oxygen index measurements and cone calorimetry to large-scale single-burning-item testsjournal article10.1002/app.46654Cellulose and other wood productsCompositesFlame retardancePolyolefinsThermal propertiesCellulose and other wood productsCompositesFlame retardancePolyolefinsThermal propertiesGeneral ChemistrySurfaces, Coatings and FilmsPolymers and PlasticsMaterials ChemistryProject IDinfo:eu-repo/grantAgreement/EC/FP7/605891/EU/High durability and fire performance WPC for ventilated façades/HIFIVENTinfo:eu-repo/grantAgreement/EC/FP7/605891/EU/High durability and fire performance WPC for ventilated façades/HIFIVENTFunding InfoEuropean Commission _x000D_ (HIFIVENT project, Research for small and medium sized_x000D_ enterprises (SMEs), grant agreement number 605891, 7th Framework_x000D_ Programme)European Commission _x000D_ (HIFIVENT project, Research for small and medium sized_x000D_ enterprises (SMEs), grant agreement number 605891, 7th Framework_x000D_ Programme)http://www.scopus.com/inward/record.url?scp=85050411501&partnerID=8YFLogxK