Evaluation of the mechanical behavior of 2001 LDSS and 2205 DSS reinforcements exposed to simultaneous load and corrosion in chloride contained concrete pore solution
No Thumbnail Available
Identifiers
Publication date
2020-09
Advisors
Journal Title
Journal ISSN
Volume Title
Publisher
Citations
Export
Abstract
The present work is focused on the study and evaluation of the mechanical properties of the new low-nickel 2001 lean–duplex stainless steel (LDSS), 2205 duplex stainless steel (DSS) and B500SD carbon steel rebars, influenced by aggressive corrosion environment. Test specimens were loaded to 85% of the yield strength while simultaneously exposed to 8 wt% Cl− concrete pore solution for 315 days. Subsequently, the specimens were loaded until failure at a high deformation rate of 0.41 mm/s. The analysis of the stress‒strain curve showed a reduction of the ultimate tensile strength greater than 35% for the B500SD, while the 2001 LDSS and 2205 DSS show a reduction lower than 20% and 10%, respectively. Analyzing elongation to failure, neither 2001 LDSS nor 2205 DSS show evidence of stress corrosion under the simultaneous action of chlorides and load. The toughness change in the 2205 DSS is negligible, the 2001 LDSS slightly reduces its resilience, and the B500SD severely decreases both properties. The fractography study revealed that 2001 LDSS and 2205 DSS show a dimple pattern with features of ductile fracture by coalescence of microvoids.
Description
Publisher Copyright: © 2020 Elsevier Ltd
Type
Citation
Briz , E , Martin , U , Biezma , M V , Calderon-Uriszar-Aldaca , I & Bastidas , D M 2020 , ' Evaluation of the mechanical behavior of 2001 LDSS and 2205 DSS reinforcements exposed to simultaneous load and corrosion in chloride contained concrete pore solution ' , Journal of Building Engineering , vol. 31 , 101456 . https://doi.org/10.1016/j.jobe.2020.101456