Browsing by Keyword "Hollow fiber spinning"
Now showing 1 - 2 of 2
Results Per Page
Sort Options
Item Fabrication of Defect-Free P84® Polyimide Hollow Fiber for Gas Separation: Pathway to Formation of Optimized Structure: Pathway to formation of optimized structure(2019-12) Etxeberria-Benavides, Miren; Karvan, Oguz; Kapteijn, Freek; Gascon, Jorge; David, Oana; Tecnalia Research & Innovation; TECNOLOGÍA DE MEMBRANAS E INTENSIFICACIÓN DE PROCESOSThe elimination of the additional defect healing post-treatment step in asymmetric hollow fiber manufacturing would result in a significant reduction in membrane production cost. However, obtaining integrally skinned polymeric asymmetric hollow fiber membranes with an ultrathin and defect-free selective layer is quite challenging. In this study, P84® asymmetric hollow fiber membranes with a highly thin (~56 nm) defect-free skin were successfully fabricated by fine tuning the dope composition and spinning parameters using volatile additive (tetrahydrofuran, THF) as key parameters. An extensive experimental and theoretical study of the influence of volatile THF addition on the solubility parameter of the N-methylpyrrolidone/THF solvent mixture was performed. Although THF itself is not a solvent for P84®, in a mixture with a good solvent for the polymer, like N-Methyl-2-pyrrolidone (NMP), it can be dissolved at high THF concentrations (NMP/THF ratio > 0.52). The as-spun fibers had a reproducible ideal CO2/N2 selectivity of 40, and a CO2 permeance of 23 GPU at 35 °C. The fiber production can be scaled-up with retention of the selectivity.Item PBI mixed matrix hollow fiber membrane: Influence of ZIF-8 filler over H2/CO2 separation performance at high temperature and pressure: Influence of ZIF-8 filler over H2/CO2 separation performance at high temperature and pressure(2020-04-15) Etxeberria-Benavides, Miren; Johnson, Timothy; Cao, Shuai; Zornoza, Beatriz; Coronas, Joaquín; Sanchez-Lainez, Javier; Sabetghadam, Anahid; Liu, Xinlei; Andres-Garcia, Eduardo; Kapteijn, Freek; Gascon, Jorge; David, Oana; Tecnalia Research & Innovation; TECNOLOGÍA DE MEMBRANAS E INTENSIFICACIÓN DE PROCESOSHigh performance and commercially attractive mixed-matrix membranes were developed for H2/CO2 separation via a scalable hollow fiber spinning process. Thin (~300 nm) and defect-free selective layers were successfully created with a uniform distribution of the nanosized (~60 nm) zeolitic-imidazole framework (ZIF-8) filler within the polymer (polybenzimidazole, PBI) matrix. These membranes were able to operate at high temperature (150 °C) and pressure (up to 30 bar) process conditions required in treatment of pre-combustion and syngas process gas streams. Compared with neat PBI hollow fibers, filler incorporation into the polymer matrix leads to a strong increase in H2 permeance from 65 GPU to 107 GPU at 150 °C and 7 bar, while the ideal H2/CO2 selectivity remained constant at 18. For mixed gas permeation, there is competition between H2 and CO2 transport inside ZIF-8 structure. Adsorption of CO2 in the nanocavities of the filler suppresses the transport of the faster permeating H2 and consequently decreases the H2 permeance with total feed pressure down to values equal to the pure PBI hollow fibers for the end pressure of 30 bar. Therefore, the improvement of fiber performance for gas separation with filler addition is compromised at high operating feed pressures, which emphasizes the importance of membrane evaluation under relevant process conditions.