Browsing by Author "Harismendy, I."
Now showing 1 - 2 of 2
Results Per Page
Sort Options
Item Effect of the biobased polyols chemical structure on high performance thermoset polyurethane properties(2022-12-16) Echeverria-Altuna, O.; Ollo, O.; Larraza, I.; Gabilondo, N.; Harismendy, I.; Eceiza, A.; POLIMEROS; Tecnalia Research & InnovationThe sustainability of the polymeric materials has become a fundamental challenge; therefore, the development of new biobased formulations has gained increasing interest. Thermoset polyurethanes (PURs) present high performance and are a competitive solution for structural composites. However, polyols used in the PUR synthesis are typically from petrochemical origin. Nowdays, a broad range of biobased polyols is available in the market, but there is not yet a specific formulation for high performance PURs composites. The aim of this work was to study the effect of biobased polyols' characteristics in the PUR processing and final properties. In addition, biobased polyol features to synthesize BIO-PURs suitable for structural applications were stablished. The viscosity and reactivity were studied by means of rheology and differential scanning calorimetry (DSC). Thermal and mechanical properties were studied through thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA) and flexural tests. The results obtained demonstrated the dramatic influence of polyols’ nature on BIO-PUR/PUR properties and their effect on the crosslink density. It was observed that using a high functionality and high hydroxyl index biobased polyol, it was possible to synthesize high performance BIO-PUR suitable for structural composites.Item Nucleation and Crystallization of PA6 Composites Prepared by T-RTM: Effects of Carbon and Glass Fiber Loading: Effects of carbon and glass fiber loading(2019-10-01) Zaldua, N.; Maiz, J.; de la Calle, A.; García-Arrieta, S.; Elizetxea, Cristina; Harismendy, I.; Tercjak, A.; Müller, A.J.; POLIMEROSThermoplastic resin transfer molding (T-RTM) is attracting much attention due to the need for recyclable alternatives to thermoset materials. In this work, we have prepared polyamide-6 (PA6) and PA6/fiber composites by T-RTM of caprolactam. Glass and carbon fibers were employed in a fixed amount of 60 and 47 wt.%, respectively. Neat PA6 and PA6 matrices (of PA6-GF and PA6-CF) of approximately 200 kg/mol were obtained with conversion ratios exceeding 95%. Both carbon fibers (CF) and glass fibers (GF) were able to nucleate PA6, with efficiencies of 44% and 26%, respectively. The α crystal polymorph of PA6 was present in all samples. The lamellar spacing, lamellar thickness and crystallinity degree did not show significant variations in the samples with or without fibers as result of the slow cooling process applied during T-RTM. The overall isothermal crystallization rate decreased in the order: PA6-CF > PA6-GF > neat PA6, as a consequence of the different nucleation efficiencies. The overall crystallization kinetics data were successfully described by the Avrami equation. The lamellar stack morphology observed by atomic force microscopy (AFM) is consistent with 2D superstructural aggregates (n = 2) for all samples. Finally, the reinforcement effect of fibers was larger than one order of magnitude in the values of elastic modulus and tensile strength.